Model(Click to view)
GB
AWS
The main purpose
ER55-G
ER80S-G
Suitable for welding high tension steels, normally applied in the construction, structural parts of bridges and pressure boiler.
ER50-G
ER70S-G
1. Used for welding all kinds of 500MPa structural steel parts, thick plates and thick pipelines.
2. Used for high speed welding on 500MPa base metals
ER50-6
ER70S-6
Used for welding all kinds of 500MPa structural steel parts. Especially for vehicles, ships, bridges, building pipes and other constructional weld.
ER50-4
ER70S-4
Used for welding all kinds of 500MPa structural steel parts. Especially for vehicles, ships, bridges, building pipes and other constructional weld.
ER50-3
ER70S-3
1. Used for welding low-carbon steel thin plates.
2. Used for welding low-carbon steel parts with thorough surface treatment.
H08MnA
EM12K
Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals
H08C
EL12
Used together with fused flux 431 or sintered fluxes 301 and 501. Used for both high speed welding and filling welding on 50kg class base metals.
H08A
EL8
Used together with fused flux 431 or sintered fluxes 301 and 501. Used for both high speed welding and filling welding on 50kg class base metals.
H08E
EL8K
Used together with fused flux 431 or sintered fluxes 301 and 501. Used for both high speed welding and filling welding on 50kg class base metals
H10Mn2
EH14
Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.
H08MN2SI
EH11K
Better choices for carbon steel and low alloy steel welding. Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.