GB：H08MN2SI
AWS：EH11K
Application：Better choices for carbon steel and low alloy steel welding. Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.：

EH11K

According with GB H08MN2SI
Corresponding with AWS EH11K
JIS W41

Introduction: It is a kind of high-manganese type welding wire. It matches with low-manganese and low-silicon type welding flux. It is not sensitive to the rust on the base metal. It has excellent bead molding and slag detachability. Monopole or dipole. AC/DC.

Applications: Better choices for carbon steel and low alloy steel welding. Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.

Chemical Composition of Welding Wire(%)

C	Mn	Si	Si	S	P
≤0.11	1.5~1.9	≤1.70-2.10	≤0.65-0.95	≤0.035	≤0.35

Mechanical Properties of Deposited Metal

Test Items	R_m	R_El/R_p0.2	A	KV₂(J)
Flux Used Together	(MPa)	(MPa)	(%)	-20℃
SJ301	480-650	≥400	≥22	≥27
HJ350	415-550	≥330	≥22	≥27

Wire Size

diameter(mm)

Φ1.6

φ3.2

φ4.0

Φ6.0