Your position is:Home>>Cast Iron Steel Electrodes

GB：EZNiCu-1
AWS：ENiCu-B
Application：Used for repair welding on gray cast iron pieces not requiring strength too much. Main Applications：：

ENiCu-B

According with GB EZNiCu-1
Corresponding with AWS ENiCu-B

Introduction: ENiCu-B is a kind of cast iron electrode with Ni-Cu alloy (Monel) core wire and strong reducibility graphite type coating. Both the welding performance and the machinability are quite similar with those of Z308. However, due to the higher shrinkage rate, the crack-resistance is worse. The welded joint has lower strength, so it is not suitable for welding force-bearing parts. It can be used for welding gray cast iron under normal temperature or preheated a little (to about 300℃). AC/DC.

Applications: Used for repair welding on gray cast iron pieces not requiring strength too much.

Chemical Composition of Deposited Metal (%)

Chemical Composition	C	Mn	Si	S	Cu	Ni	Fe	Total Quantity of Other Elements
Guarantee Value	≤1.00	≤2.50	≤0.80	≤0.025	24~35	60~70	≤6	≤1.00

Reference Current (AC, DC+)

Electrode Diameter(mm)	φ2.5	φ3.2	φ4.0	φ5.0
Welding Current (A)	50~100	70~120	110~170	140~190

Instructions:
1.The electrodes must be baked under about 150℃ for an hour before welding.
2.When welding, stringer bead is suitable in the manipulation of electrodes. Every time, the weld length is suitable when lower than 50mm. The welded places should be hammered light quickly after welding so as to eliminate the stress in the welded areas and avoid cracks.

Packing details: In carton of 20kgs/net, consisting of 8 boxes x 2.5kgs for 2.5mm, & 4 boxes x 5kgs for other sizes.

With/ without pallets (Fumigation-free pallets) upon customer’s request.

pace="False" Negative="False" NumberType="1" TCSC="0" w:st="on">150℃ for an hour before welding.
2. Hammering the weld gently, the stress in the welded areas can be eliminated and cracks can be avoided.

Packing details: In carton of 20kgs/net, consisting of 8 boxes x 2.5kgs for 2.5mm, & 4 boxes x 5kgs for other sizes.

With/ without pallets (Fumigation-free pallets) upon customer’s request.

und:white;padding:.75pt .75pt .75pt .75pt'>

100~160

140~200

Instructions:
1.The electrodes should be baked under 200-250℃ for an hour before welding.
2.D/C is the first choice and the current should not be too strong.

Packing details: In carton of 20kgs/net, consisting of 8 boxes x 2.5kgs for 2.5mm, & 4 boxes x 5kgs for other sizes.

With/ without pallets (Fumigation-free pallets) upon customer’s request.